Description:
- ATLAS GEOFLEX adhesive formulation uses the innovative technology of silicate gel. The silicate gel has the unique ability to bind water. The gel fills the pores formed at the stage of adhesive setting through the network of inorganic bonds. Accumulation of a part of the mixing water ensures complete cement hydration, regardless of the type of the tiles. Thanks to appropriate water management, which is necessary to complete the setting process, the gel adhesive ensures full adhesion to substrates of various absorbency levels. The use of silicate gel technology offers the following benefits:
- the possibility of fitting any type of cladding, both absorbent and non-absorbent,
- it is possible to adjust the consistency of the adhesive to the individual preferences of the contractor and the needs of the project, by dosing water over a much wider range than with traditional adhesives
- safe bonding of tiles on substrates exposed to direct sunlight, both during tiling work and while the adhesive mortar is setting (e.g. on balconies, terraces, etc.).
Main properties:
- deformability S1
- for the most demanding substrates – OSB, floors with underfloor heating
- grouting is possible after just 12 h
- No cladding run-off – provides the opportunity to glue the cladding from the top, without the need to support it at the installation stage.
- High stability of large-format tiles (even with an area of more than> 5 m2) laid on horizontal substrates – the tiles do not sink in the mortar layer.
- 3 in 1 evening-up / tile application / evening-up and tile application in one step
- application temperature 5-35 degrees
- for micro, small, medium, large and XXL tiles
- foil bag
MAin parameters
layer thiknes: 2 – 15 mm
laying temperature: od +5 °C do +35 °C
ready in: approx. 4 hrs
bonding: after 12 hrs
Tile type:
glazura i terakota +
gres porcelain +
natural stone recommended patch test
glass tiles, tinted, printed etc. recommended patch test
Substrate:
tiles or stone (tile on tile) +
underfloow heating, water or electric +
hydroisolation+
cement based flooring
+
cement based plasters, cement+minetal mortars +
gypsum based mortars in dry areas +
gypsum based mortars in damp and wet areas +
plaster boards +
concrete +
terazzo +
OSB/3 boards , OSB/4 boards +
Consumption
Average consumption is based on application on a straight flat substrate If the substrate is highly textured the consumption will increase. When using the combination tiling method the consumption will increase significantly.
Average consumption:
- Mosaic tiles 2x2cm fitted on the wall, trowel notch 4mm, 1.3 kg/m2
- Tiles 30x60cm fitted on the wall, trowel notch 8mm, 2.5 kg/m2
- Tiles 60x60cm fitted on the floor, trowel notch 12mm, 3.5 kg/m2
- Tiles 90x90cm fitted on the floor, trowel notch round 12mm, 4.6 kg/m2
- “Wood Parquet” Tiles e.g. 20x90cm fitted on the floor, trowel notch 12mm, 4.6 kg/m2 (semi-liquid texture – 8.25 l water per 25 kg adhesive)